Corrosion is the primary factor affecting the longevity and reliability of pipelines that transport crucial energy sources throughout the global. The average annual corrosion-related cost is estimated at $7 billion to monitor, replace, and maintain these assets. The corrosion-related cost of operation and maintenance makes up 80% of this cost. Learn how to prevent, mitgate and reduce corrosion cost. 



Corrosion is a natural process where refined materials react with their environment, and revert to a more chemically-stable form. Below we discuss some of the most common topics and questions surrounding corrosion.


Table of Contents

  1. Basics of Corrosion
  2. The Galvanic Series
  3. Cathodic Protection Design
  4. Pipeline Corrosion Protection with Isolation
  5. What is External and Internal Corrosion?
  6. What was the Impact of Pipeline Incidents?
  7. Why do we put Pipes Below Grade?  What Challenges Does it Present?
  8. How does Electrical Isolation help Prevent Corrosion?
  9. What Applications Require Electrical Isolation?
  10. What are Common Causes for Isolation Failures?


Want us to Email You a Copy?

No problem! Just enter your email address below and we'll provide you with a download.

Or you can read the full guide without giving us your email, simply keep scrolling.

1 Start 2 Complete
GPT | Pipeline Corrosion Prevention Download

Basics of Corrosion

Corrosion is a constant force in industries from Oil & Gas production, Maritime, to construction of highways, bridges, pipelines, & any underground systems. Corrosion is a natural process where refined materials react with their environment, and revert to a more chemically-stable form. The rate of corrosion is dependent on a number of environmental variables, but for corrosion to occur four basic elements are required (Anode, Cathode, Metallic Path, and Electrolyte).

In the fight against corrosion, integrity engineers focus on removing the presence of one or more of these basic elements. The first defense against corrosion is a coating system which helps to protect the asset from the surrounding electrolyte. Coatings are typically used as a barrier coating, protecting the substrate from contact with the Electrolyte. In addition to serving as a barrier, some coatings also use inhibitive, or sacrificial pigments, causing passivation, or a sacrificial anode to form at any Coating Holidays or defects.

Integrity engineers must also utilize cathodic protection (impressed or passive) to protect assets, as coatings can be damaged, which can amplify corrosion locally at the defect (Coating Holiday, cracking, etc.). Cathodic protection systems combat corrosion by converting all of the anodic (active) sites on the metal surface of an asset to cathodic (passive) sites by supplying electrical current (or free electrons) from an alternate source to equalize the potential on the surface of the metal structure (left).

The Galvanic Series

Materials are listed from most Noble (passive), to most electronegative (active) in the Galvanic series. In reference to the below graphic, Magnesium is the most active. When two metals are coupled, the more active will share electrons with the more noble material causing an oxidation reaction (rust) at the electronegative material, and a reduction reaction at the more electropositive (noble) material.

Cathodic Protection Design

CP does not eliminate corrosion, but actually transfers corrosion current from the protected structure (asset) to the cathodic protection anode. This is the case in Galvanic (Sacrificial) anode systems, and impressed current system.

A sacrificial anode system is easily installed, requires no external electricity, and minimal right-of-way cost. The limitations of sacrificial anodes are current output, require anodes to be replaced once an anode has been spent / consumed, and a higher cost per unit ampere than impressed current. Based on the above characteristics, galvanic systems are used in specific applications (offshore, within vessels, or in an area with many other metallic structures). Galvanic anodes are commonly used in combination with impressed current systems at problem/ repair areas, shorted casings, cathodic interference / stray current discharge points, areas influenced by electrical shielding, and locations with significant coating damage.

Impressed current systems are comprised of an external power source and anodes. The power source (rectifier) forces current to flow from the anode to the structure to through the electrolyte. 

Pipeline Corrosion Protection with Isolation

Pipe and the metallic pipeline components are supplied coated (Valves, Fittings, etc.). Following welding, and inspection field applied epoxies are used to cover exposed weld bevels.

What is Pipeline Isolation?

In metallic pipelines, corrosion is the constant attempt by nature to reduce pipelines to their original oxide state. It is an electrochemical reaction that has four parts: anode, cathode, metallic path and electrolyte. Flange isolation and joint isolation are a means of preventing electrochemical reactions from occurring between two dissimilar metals by breaking the metallic path, or preventing the current in a cathodic protection (CP) from traveling beyond the area intended to be protected by the CP system. ;

In addition Cathodic protection (CP) systems are used to supply extra electrons causing the asset to be a passive location or a cathode. In order to control what is protected by these electrons, isolation is used as the ‘bookends’ of a CP system. Isolation will allow you to protect specific assets, and eliminate any dissimilar metals connection. An example would be a pipeline coming into a compressor station, the role of the CP system is to protect the pipeline, but not the compressor station. Isolation would be used on either side of the compressor station to avoid the large metallic compressor station draining the CP current.

What is External Corrosion?

External corrosion occurs due to environmental conditions on the exterior surface of the steel pipe that can cause an electrochemical interaction between the exterior of the pipeline and the soil, air, or water surrounding it. Galvanic and atmospheric corrosion are common types of external corrosion.


What is Internal Corrosion?

Internal corrosion occurs due to a chemical attack on the interior surface of a steel pipe from the products transported in the pipe. This can be from either the commodity transported, or from other materials carried along with the commodity, such as water, hydrogen sulfide, and carbon dioxide.


Is Natural Gas Corrosive?

Natural Gas can mean gas containing methane, Ethane, H2S, water, and COS, and other components. Natural Gas will be corrosive because of the H2S and water. Commercial Natural Gas is treated, and it is no longer corrosive.


What is PHMSA?

PHMSA is a portion of the DOT. PHMSA is the Pipeline and Hazardous Materials Safety Administration. Est. 1970.


How Many Pipeline Failures are the Result of Corrosion?

Data shows that from 1998-2017 approximately 18% of pipeline incidents on average were caused by corrosion, learn more here.

Case Study


Cenovus Energy High Pressure Separator - VCXT


Discover how flange face corrosion can occur on the flanges of a carbon steel separator when a standard spiral wound gasket is between the unit and the stainless steel piping system.


What was the Impact of Pipeline Incidents?

Why do we Put Pipes Below Grade?  What Challenges Does it Present?

While there are above ground pipelines, most notably the Trans-Alaska Pipeline System (TAPS). The significant majority of pipelines are buried. Pipelines are often located below grade due to permitting requirements in order to minimize the impact to the surrounding communities by concealing it from view. Pipelines will come above ground for pump stations, valves, and other equipment requiring access.

Locating pipelines below grade introduces the pipeline into constant contact with an Electrolyte, one of the four elements needed for a corrosion cell. The first line of defense is a Barrier Coating, which creates a barrier between the Electrolyte and the metallic structure.

How Does Electrical Isolation Help Prevent Corrosion?

Electrical Isolation in a pipeline system is achieved by installing Flange Isolation Kits (FIKs), or Monolithic Isolation Joints (MIJs) in line to separate equipment or pipeline segments. FIKs & MIJs utilize materials with resistance to electrical current in order to block the transfer of electrons, effectively eliminating the metallic path, one of the four elements needed for a corrosion cell.

What Applications Require Electrical Isolation?

Electrical Isolation is used to break up pipeline segments to optimize current output from rectifiers in Impressed current cathodic protection systems. It is advantageous to break up long pipeline runs with isolation to improve efficiency, and minimize the impact of maintenance or repair on the pipeline.

Electrical Isolation is also used to prevent interference or damage to electronics, which may be found in valves, sensors, compressor stations, and other equipment.

Electrical Isolation should also be used in the presence of any dissimilar metal connection to prevent a galvanic coupling.

What are Common Causes for Isolation Failures?

Failure of electrical isolation gasket, joint, or union can be caused by environmental factors, mechanical forces exerted on the pipeline system, or improper installation. The likelihood of failure due to environmental factors can be controlled by the materials used.

A variety of materials are used to provide electrical isolation within a pipeline systems. The different materials have different characteristics which impact their efficacy (Electrical Resistance, Water absorption, Dielectric Strength, Permeability, Temperature range, Chemical Resistance, Compressive strength).

Electrical resistance is a measure of how well a material resists electrical current.  

Isolation materials which have a high water absorption will be impacted by humidity, rainwater, and snowmelt. The moisture within the isolation material will cause a significant reduction in the electrical resistance. In conditions with temperatures fluctuating from above to below freezing also have the potential for cracking of the isolation material.

White Paper


Advancing Corrosion Control


Corrosion costs the global oil and gas industry billions of dollars a year and that a significant contributor to these costs are due to galvanic corrosion in flanged piping systems. Tim Hurley, from GPT Industries, explains how fibreglass reinforced epoxy products can be used to prevent galvanic corrosion in flanged piping systems.